Comparison of Two Mechanical Alloying Synthesis of WMoTaNbCr and WMoTaNbTi

Ignacio Orellana Araya, Claudio Aguilar Ramírez*

Mechanical alloying is a route that prevents the common dendrite structure with segregation and avoids the problems related to the grain growth present in arc melting, besides allowing the alloying of elements with a high melting point at room temperature and limited solubility. In this study, the phase evolution of two refractory high entropy alloys was developed, WTaMoNbCr and WTaMoNbTi, in two different conditions of mechanical alloy: with detentions intervals and continuous mechanical alloying. The first one produces the face-centered cubic single solid solution WTaMoNbCr and WTaMoNbTi with lattice parameters 0.4313 and 0.4305 nm, respectively. The second mechanical alloying produced a widening of the lattice parameter to 0.4319 and 0.4325 nm of the WTaMoNbCr and WTaMoNbTi, respectively, due to the high contamination related to the process.

குறியிடப்பட்டது

Index Copernicus
ஜே கேட் திறக்கவும்
கல்வி விசைகள்
ஆராய்ச்சி பைபிள்
CiteFactor
காஸ்மோஸ் IF
RefSeek
ஹம்டார்ட் பல்கலைக்கழகம்
அறிஞர்
சர்வதேச புதுமையான இதழ் தாக்க காரணி (IIJIF)
சர்வதேச அமைப்பு ஆராய்ச்சி நிறுவனம் (I2OR)
காஸ்மோஸ்
மருத்துவக் கல்வி மற்றும் ஆராய்ச்சிக்கான ஜெனீவா அறக்கட்டளை
ரகசிய தேடுபொறி ஆய்வகங்கள்

மேலும் பார்க்க