Structural Investigations of Cr3+ Ions Doped Alkali Lead Zinc Phosphate Glasses

S Sreehari Sastry, MVVK Srinivas Prasad, B Rupa Venkateswara Rao

Lead zinc phosphate glasses containing 0.1% transition metal ion Cr3+ were prepared by melt quenching technique and their amorphous nature confirmed by X-Ray diffraction. The covalent bond nature of Cr3+ ions with octahedral symmetry in glass network was established through Electron Paramagnetic Resonance and optical absorption spectroscopic studies. Endothermic dip for glass transition temperature (Tg) at about 410 0C and an exothermic peak subsisted from thermal studies were obtained. De-polymerization of host glass network due to addition of alkali content to the glass matrix, has turned as a strong candidate for nonlinear optical laser applications

குறியிடப்பட்டது

கல்வி விசைகள்
ஆராய்ச்சி பைபிள்
CiteFactor
காஸ்மோஸ் IF
RefSeek
ஹம்டார்ட் பல்கலைக்கழகம்
அறிவியல் இதழ்களின் உலக பட்டியல்
அறிஞர்
சர்வதேச புதுமையான இதழ் தாக்க காரணி (IIJIF)
சர்வதேச அமைப்பு ஆராய்ச்சி நிறுவனம் (I2OR)
காஸ்மோஸ்

மேலும் பார்க்க